The ZnS:Cu,Cl thick film electroluminescent devices with the stacking type(separated with phosphors and insulator layers) and the composite type (mixed with phosphor and insulator materials) emission layers were fabricated on ITO/glass substrates by the screen printing methods. The opical and electrical properties were investigated as fundations of applied voltages and frequencies. In the stacking type, the luminance was about 58 cd/ \m 2 at the applied voltage of 400Hz, 200V and increased to 420 cd/ \m 2 with increasing the frequency to 30Hz. For the composite type devices, the threshold voltage was 45V and the maximum luminance was 670 cd/ \m 2 at the driving condition of 200V, 30Hz. The value of luminance of the composite type device showed 1.5 times higher than that of stacking type device. The main emission peak was 512 nm of bluish-green color at 1Hz frequency below and shifted to 452 nm in the driving frequency over 5Hz showing the blue omission color. There were no distinct differences of the main emission peaks and color coordinate for both samples.