Higher operating temperatures increase efficiency of the concentrating solar power plants but promote faster corrosion of the pipes and vessels made of Hastelloy or stainless steel materials for the molten-salt mixtures. Hastelloys C-276 and C-22 and stainless steel 304 coupons evaluated in the present study in a eutectic molten salt consisting of 13.4 mol% NaCl, 33.7 mol% KCl and 52.9 mol% ZnCl2 showed substantially lower corrosion rates in the absence versus presence of air from 200 to 800 degrees C as determined by electrochemical and gravimetric methods. In the presence of air, the corrosion rate for the Hastelloy C-276 in the molten salt was found to diminish with immersion time and converges around similar to 50 mu m per year after 4 weeks of immersion at 500 degrees C, which is close to the value similar to 40 mu m per year obtained using the electrochemical method at 500 degrees C. For anaerobic corrosion rate estimation, the corrosivity of an alloy sample was examined by immersing in molten salt inside a sealed quartz container without any contact with air, which is possible because the vapor pressure of the eutectic molten salt is only about 0.7 atm at 800 degrees C. The corrosion rate of the Hastelloy C-276 was only 10 mu m per year in the molten salt in the absence of air at 800 degrees C, which is extremely low compared to 500 mu m per year in conducting corrosion studies in the presence of air at 800 degrees C. The Hastelloy coupons after immersion testing in the absence of air have then been examined also by SEM, and the images did not show any significant changes in the surface. This behavior indicates that, from a corrosion standpoint, the eutectic molten salt in the absence of air is suitable as a heat transfer fluid in Hastelloy C-276 pipes and containers up to 800 degrees C. (C) 2015 Elsevier Ltd. All rights reserved.