Carbon nanotubes (CNTs) were functionalized with Lanthanum (La) modifier and appropriate acid-treatment methods. CNT-containing film was deposited on silicon substrates via a self-assembly process. The formation and microstructure of La treated CNTs and CNT-containing film were characterized by high-resolution transmission electron microscopy (HRTEM), scanning electron microscopy (SEM), X-ray photoelectron spectrometry (XPS) and water contact angle (WCA). Its tribological properties were evaluated with a UMT-2MT reciprocating friction tester. The results show that CNTs were adsorbed on silicon substrates by means of chemically bonding between La and oxygen-containing functional groups. The friction coefficient of the silicon substrates is reduced from 0.87 to 0.12 after the deposition of CNT-containing film on its surface. CNT-containing film shows excellent antiwear, friction reducing ability and load-carrying capacity due to excellent mechanical and self-lubrication properties of CNTs. (C) 2015 Elsevier B.V. All rights reserved.