The electrical conductivity and morphology of thick (up to 3 mm) porous polypyrrole (PPy) layers produced electrochemically from pyrrole in acetonitrile (ACN) solutions have been studied. The electrical conductivity of pressed porous layers ranges from 1 to 10 S cm-1, which is about one order of magnitude less than that in films which were prepared under similar conditions but without PnClCr. Analysis of the temperature dependence of conductivity has confirmed the major role of hopping in relation to tunnelling in charge transport inside the PPy layers even at lower temperatures. Scanning electron microscopy (SEM) showed a globular structure, which is different from the usual cauliflower-like structure of PPy films prepared without any oxidizing agent. Globular particles of about 1-3 mum diameter have been found under a thin smooth crust on the electrode side of the sample. Globular particles form linked chain-like or larger round formations poorly filling the space. Closely packed fibrils of about 20 nm diameter and over 100 nm in length were found inside the aggregates.