Electrochemical exfoliation technique using the pyrophosphate anion derived from tetra sodium pyrophosphate was employed to produce graphene. As-synthesized graphene was then drop dried over a cold rolled Cu sheet. Ni coating was then electrodeposited over bare Cu and graphene-Cu substrates. Both substrates were then isothermally annealed at 800 degrees C for 3 h. WDS analysis showed substantial atomic diffusion in annealed Ni-Cu sample. Cu-graphene-Ni sample, on the other hand, showed negligible diffusion illustrating the diffusion barrier property of the graphene coating. (C) 2016 Elsevier B.V. All rights reserved.