The structure and mechanical properties of Al-Li8090 alloy, that was dynamically deformed and then age hardened, were studied as a function of the changes in the nature and amount of precipitates produced. A comparison was made between two groups of samples, one group that was solution heat treated (SHT) and quenched from 530 degrees C before the dynamic deformation and the other group that was dynamically deformed in the as-received (AR) condition. The higher values for microhardness and ultimate tensile strength observed (138 and 140 VHN, and 405 and 458 MPa, respectively), subsequent to shock treatment (ST), have been attributed to the increase in dislocation density and grain-boundary precipitation produced due to shock deformation. Dislocations and grain boundaries were assumed to act as precipitation sites and an increase in dislocation density, due to ST, was expected to increase precipitation density of delta’(Al3Li), S(Al2CuMg), and T-1(Al2CuLi) phases which, in turn, are expected to increase strength properties of the alloy. Differential scanning calorimetry showed that, for the species that precipitate below 180 degrees C, delta’(Al3Li) and GP zones, an increase in the amount of deformation increased the precipitation temperatures. However, for the species that precipitate at 197 degrees C, S(Al2CuMg), an increase in the amount of deformation produced a decrease in its precipitation temperature. These results have been partially confirmed by the activation energy calculations for temperatures below 197 degrees C, which show a decrease of precipitation energies with an increase in the amount of deformation. Activation energies calculated from ageing curves showed that when ageing at low temperature (165-180 degrees C range), activation energies for the precipitation process are decreased upon increase in cold work. Shock treatment of SHT samples exhibited decreased activation energy values of precipitation, from 36.14 kcal mol(-1) for the SHT sample to 24.18, 24.08, and 21.00 kcal mol(-1) for SHT + ST samples 1, 2, and 3, respectively (corresponding to 1, 2, and 3 sheets of explosive). Activation energies of precipitation for AR + ST samples showed even lower values; 9.45, 9.95, and 8.21 kcal mol(-1) for samples 4, 5, and 6, respectively. These activation energies strongly corroborate the role of defect substructure on the age-hardening kinetics of this alloy.