Micro/nanofibrous structures have been applied widely in various tissue-engineering applications because the topological structures are similar to the extracellular matrix (ECM), which encourages a high degree of cell adhesion and growth. However, it has been difficult to produce a three-dimensional (3D) fibrous structure using controllable macro-pores. Recently, cellulose has been considered a high-potential natural-origin biomaterial, but its use in 3D biomedical structures has been limited due to its narrow processing window. Here, we suggest a new 3D cellulose scaffold consisting of multi-layered struts made of submicron-sized entangled fibers that were fabricated using an electrohy-drodynamic direct jet (EHDJ) process that is spin-printing. By optimizing processing conditions (electric field strength, cellulose feeding rate, and distance between nozzle and target), we can achieve a multi-layered cellulose structure consisting of the cylindrically entangled cellulose fibers. To compare the properties of the fabricated 3D cellulose structure, we used a PCL fibrous scaffold, which has a similar fibrous morphology and pore geometry, as a control. The physical and in vitro biocompatibilities of both fibrous scaffolds were assessed using human dermal fibroblasts, and the cellulose structure showed higher cell adhesion and metabolic activities compared with the control. These results suggest the EHDJ process to be an effective fabricating tool for tissue engineering and the cellulose scaffold has high potential as a tissue regenerative material. (C) 2015 Elsevier Inc. All rights reserved.