Dislocations in FCC structure are dissociated into two partial dislocations. The dissociation width of a dissociated dislocation controls the mechanical behavior of the alloy. Experimental work using transmission electron microscopy on factors determining the dissociation width is reviewed with special reference to the Suzuki segregation.