Stoichiometric SrTiO3 (STO) films doped with Fe or Cr were prepared by r.f. magnetron sputtering technique. The effects of Fe or Cr doping in the SrTiO3 films were studied on the leakage current property which was discussed by defect chemistry. The experimental results can be explained by a model in which oxygen vacancies are the key defects responsible for the leakage current. Acceptor doping, with a small concentration of Fe or Cr, has led to a substantial improvement to 10(-9) order in the leakage current density. Above the concentration of 0.01 similar to 0.02 mol % Fe2O3, Cr2O3, however, as the concentration increased, the leakage current increased. These acceptors in Ti4+ site are expected to electrically compensate for donor species such as oxygen vacancies, thereby reducing the concentration of mobile carriers that contribute to electrical conduction. Consequently, acceptor doped STO films have been shown to be superior to undoped films for applications requiring high leakage resistance, such as dynamic random access memory capacitors.