Although stereocomplex (sc) crystallization is highly effective for improving the thermal resistance of poly(lactic acid) (PLA), it is much less predominant than homocrystallization in high-molecular-weight (HMW) poly(D-lactic acid)/ poly(D-lactic acid) (PLLA/PDLA) racemic blends. In this contribution, the sc crystallization of HMW PLLA/ PDLA racemic blends was facilitated by using comblike PLAs with cellulose acetate as the backbone. Competing crystallization kinetics, polymorphic crystalline structure, and structural transition of comblike PLLA/PDLA. blends with a wide range of MWs were investigated and compared with the corresponding linear/comblike and linear blends. The HMVV comblike blend is preferentially crystallized in sc polymorphs and exhibits a faster crystallization rate than does the corresponding linear blend. The sc crystallites are predominantly formed in nonisothermal cold crystallization and isothermal crystallization at temperatures above 120 C for the comblike blends. Except for the facilitated sc formation in primary crystallization, synchrotron radiation WAXD analysis indicates that the presence of a comblike component also facilitates the transition or recrystallization from homocrystallite (hc) to sc crystallite upon heating. Preferential sc formation of comblike blends is probably attributable to the favorable interdigitation between enantiomeric branches and the increased mobility of polymer segments. After crystallization under the same temperature, the comblike blends, which mainly contain sc crystallites, show smaller long periods and thinner crystalline lamellae than do the corresponding PLLA with homocrystalline structures.