Spinel lithium manganese oxide, LiMn2O4, is a promising cathode for lithium ion battery in large-scale applications, because it possesses many advantages compared with currently used layered lithium cobalt oxide (LiCoO2) and olivine phosphate (LiFePO4), including naturally abundant resource, environmental friendliness and high and long work potential plateau. Its poor cyclability under high temperature, however, limits its application. In this work, we report a significant cyclability improvement of LiMn2O4 under elevated temperature by using dimethyl phenylphonite (DMPP) as an electrolyte additive. Charge/discharge tests demonstrate that the application of 0.5 wt.% DMPP yields a capacity retention improvement from 16% to 82% for LiMn2O4 after 200 cycles under 55 degrees C at 1 C (1C = 148 mAh g(-1)) between 3 and 4.5 V. Electrochemical and physical characterizations indicate that DMPP is electrochemically oxidized at the potential lower than that for lithium extraction, forming a protective cathode interphase on LiMn2O4, which suppresses the electrolyte decomposition and prevents LiMn2O4 from crystal destruction. (C) 2015 Elsevier B.V. All rights reserved.