An insightful study on the fundamental lithium storage behavior of all-solid-state lithium battery with a structure of LiNi0.8Co0.15Al0.05O2 (NCA)/Li10GeP2S12/Li-In is carried out in this work. The relationship between electrochemical performances and particle size, surface impurities and defects of the NCA positive material is systematically investigated. It is found that a ball-milling technique can decrease the particle size and remove surface impurities of the NCA cathode while also give rise to surface defects which could be recovered by a post-annealing process. The results indicate that the interfacial resistance between the NCA and Li10GeP2S12 is obviously decreased during the ball-milling followed by a post-annealing. Consequently, the discharge capacity of NCA in the NCA/Li10GeP2S12/Li-In solid-state battery is significantly enhanced, which exhibits a discharge capacity of 146 mAh g(-1) at 25 degrees C. (C) 2016 Elsevier B.V. All rights reserved.