Dual-carbon enhanced Si-based composite (Si/C/G) has been prepared via employing the widely distributed, low-cost and environmentally friendly Diatomite mineral as silicon raw material. The preparation processes are very simple, non-toxic and easy to scale up. Electrochemical tests as anode material for lithium ion batteries (LIBs) demonstrate that this Si/C/G composite exhibits much improved Li-storage properties in terms of superior high-rate capabilities and excellent cycle stability compared to the pristine Si material as well as both single-carbon modified composites. Specifically for the Si/C/G composite, it can still deliver a high specific capacity of about 470 mAh g(-1) at an ultrahigh current density of 5 A g(-1), and exhibit a high capacity of 938 mAh g(-1) at 0.1 A g(-1) with excellent capacity retention in the following 300 cycles. The significantly enhanced Li-storage properties should be attributed to the co-existence of both highly conductive graphite and amorphous carbon in the Si/C/G composite. While the former can enhance the electrical conductivity of the obtained composite, the latter acts as the adhesives to connect the porous Si particulates and conductive graphite flakes to form robust and stable conductive network. (C) 2016 Elsevier B.V. All rights reserved.