Herein, two new two-dimensional Nb4C3-based solid solutions (MXenes), (Nb-0.8,Ti-0.2)(4)C3Tx and (Nb-0.8,Zr-0.2)(4)C3Tx (where T is a surface termination) were synthesizedas confirmed by X-ray diffractionfrom their corresponding MAX phase precursors (Nb-0.8,Ti-0.2)(4)AlC3 and (Nb-0.8,Zr-0.2)(4)AlC3. This is the first report on a Zr-containing MXene. Intercalation of Li ions into these two compositions, and Nb4C3Tx was studied to determine the potential of those materials for energy storage applications. Lithiation and delithiation peaks at 2.26 and 2.35 V, respectively, appeared in the case of Nb4C3Tx, but were not present in Nb2CTx. After 20 cycles at a rate of C/4, the specific capacities of (Nb-0.8,Ti-0.2)(4)C3Tx and (Nb-0.8,Zr-0.2)(4)C3Tx were 158 and 132 mAh/g, respectively, both slightly lower than the capacity of Nb4C3Tx.