A chiral bio-absorbent of Fe-CoNiP coated on the spirulina was fabricated by the electroless and chemical vapor decomposition. The scanning electron microscopy (SEM) was used to evaluate the spirulina cells particle morphology. X-ray diffraction (XRD) patterns were done to analyze the particle crystal grain structure. The permittivity and permeability was measured by a vector network analyzer in frequency 8-18 GHz, and the reflection loss (RL) was calculated. The results showed the carbonyl iron particles (CIPs) and CoNiP were bonded to the spirulina surface, the permittivity and permeability could be enlarged as Fe films coated on the particles compared with the CoNiP spirulina, it was attributed to the excellent electromagnetic property of CiPs. The chiral Fe CoNiP composites had a better absorbing property at 8-18 GHz than the CoNiP spirulina composite, the RL was -16.26 dB at 10.48 GHz, the absorbing band was 9.5-11.5 GHz of RL less than 10 dB, which indicated the Fe-CoNiP spirulina could be an effective absorbent used in 8-18 GHz. (C) 2015 Elsevier B.V. All rights reserved.