New developments of fluidized beds are focusing on their use in powder circulation systems for thermal energy capture, storage and re-use. Although fast particle motion and associated high degree of mixing favor the high rate of heat transfer in fluidized beds, they however cause inter-particle collision and bed-to-wall impacts, both leading to particle attrition. Experimental work on attrition was carried out in batch gas fluidized beds of 6.62 cm and 10 cm I.D. The rate of attrition was determined both for bubbling fluidized bed conditions, and when adding jet-orifices above the distributor. The attrition was determined from the variation in-composition of bed material and collected carryover. A literature survey determined the dominant fluidization parameters, including operating superficial gas velocity, orifice velocity and size, bed weight and diameter, and particle characteristics. Analysis of the experimental findings resulted in a correlation that encompasses all relevant operating characteristics. As a result, the attrition rate can be correlated as the sum of the bubble-induced and jet-induced contribution: R-t = K-1[gamma(U-U-mf).W/D] + K-2[n(or).d(or)(2)] with K-1 and K-2, the intrinsic attrition rate constants, being mainly a function of particle characteristics. K-1 is similar to 10(-5) for soft, similar to 10(-6) for hard and similar to 10(-7) for very hard particles, respectively. k(2) is similar to 10(-5) for silica sand. In general, attrition ismegligible at low superficial gas velocities, but significantly increases through the jet-induced contribution if the orifice velocity exceeds similar to 30 m/s. (C) 2015 Elsevier B.V. All rights reserved.