In this study, paraffin was selected as the phase change materials (PCMs) and rude-Palygorskite (Pal), rinsed-Pal, H+-Pal and organic-Pal were selected as porous materials. A series of paraffin/Pals composite PCMs were prepared by direct impregnation method without vacuuming. In the composite PCMs, up to 150 wt% of paraffin could be loaded in H+-Pal. The Differential Scanning Calorimetry (DSC) tests revealed that paraffin/ H+-Pal composite PCM had a melting temperature of 54-56 degrees C and latent heat of 132.18 J g(-1). In addition, the composite PCMs were characterized by Scanning Electron Microscope (SEM), Brunauer, Emmett, and Teller (BET) and Fourier Transform Infrared Spectroscopy (FTIR). Good thermal stability was observed for composite PCMs by cycling test; we found that paraffin/H+-Pal composite PCM maintained similar to 95% of the initial latent heat after the cycling test. In conclusion, the impregnation of Pals with paraffin was a promising method for preparation of excellent PCM composites. (C) 2015 Elsevier B.V. All rights reserved.