Polyurethanes (PUs) and polyurethane-ureas (PUUs), with good mechanical stability and the possibility of tuning the gas transport properties are promising materials for selective gas separation membranes. Here, we synthesized various types of PUs and PUUs with polytetramethylene glycol (PTMG), isophorone diisocyanate (IPDI) and different ethereal chain extenders (1:3:2 M ratio). FTIR and DSC results showed that the phase separation would vary in PUs and PUUs structures by changing the length and functionality of the chain extenders. More mixing was inferred for PUs and PUUs with high ethereal content. In contrast, phase separation was more likely with increases in the chain extender length. Pure (CO2, CH4, O-2 and N-2) and mixed gas (CO2:N-2 (50:50 vol%) and CO2:CH4 (50:50 vol%)) permeation measurements correlated well with the phase separation in the polymer structure. The octanediamine-based PUU with the highest amount of phase separation showed the highest permeability (160 barrer for CO2 and CO2/N-2 selectivity of 30). On the other hand, the 3,6-dioxa- 1,8-octanediol- based PU, despite having the same chain extender length as octanediamine-based PUU, presented the lowest phase separation and gas permeability (62 barrer for CO2 and CO2/N-2 selectivity of 29). (C) 2016 Elsevier B.V. All rights reserved.