The core/shell structure was formed by GO self-assembled with amine-functionalized commercial ZnO (CZO) and preparative hexagonal ZnO (HZO), respectively. Graphene-coated CZO and HZO were obtained after being reduced in Ar at 500 degrees C. The mechanism of the coating procedure was investigated by measuring their respective zeta potential values. Our characterizations demonstrate that graphene on HZO has better quality and fewer layers. An obvious band gap decrease of ZnO was observed for coating with graphene. Photoluminescence spectra of ZnO@graphene core/shell composites display the fluorescence quenching property, which indicates its good application prospect in optoelectronics, photocatalytic and other fields. (C) 2016 Elsevier B.V. All rights reserved.