Fe70Pd30 nanostructures have potential application in actuators due to their conventional and magnetic shape memory. Here, we report the microstructure of electrodeposition grown Fe-Pd nanowires in which the process was confined to polycarbonate membranes with a nominal pore diameter of 200 nm. We used an acid electrolyte (pH approximate to 5) in which the solution was stabilized with sulfosalicylic acid. The average chemical concentration of the nanowires can be systematically shifted from rich palladium to rich iron by changing the growth potential. The study of the microstructure by transmission electron microscopy indicates high chemical inhomogeneities due to phase coexistence between rich palladium regions (with FCC structure) and rich iron regions. The latter present a combination of BCC and amorphous phases. The average chemical composition of the nanowires can be better adjusted by using a low frequency square wave voltage excitation (alternating rich Pd and rich Fe regions). However, independently of the growth process, the nanowires morphology collapses after thermal annealing. This could be ascribed to fragile grain boundaries due to the presence of amorphous hydroxides and chemical impurities produced during the electrochemical process. (C) 2016 Elsevier B.V. All rights reserved.