Oxide ion conductivity in doped NdBaInO4 with new type oxygen deficient perovskite was studied and it was found that doping Ti to In site is effective for increasing the oxide ion conductivity. Since increasing amount of doped Ti increased the partial electronic conductivity under reducing atmosphere, the optimized amount of Ti doped for In site exists around 20 mol%, namely, NdBaIn0.8Ti0.2O4. The estimated transport number of oxide ion in this optimized composition was higher than 0.8 from H-2-O-2 oxygen concentration cell, however, it is lower than 0.1 from N-2-O-2 cell because the hole conduction is dominant in high P-O2 range. Consequently, although the oxide ion conductivity is around log(sigma/scm(-1)) = -2.5 at 1173 K, this study reveals that Ti doped NdBaInO4 which is unique edge oxygen facing structure, is a new family of oxide ion conductor. (C) 2016 Elsevier B.V. All rights reserved.