The hydrophilicity of:titanium dioxide has been investigated for films, deposited on glass by e-beam evaporation, being exposed to UV radiation and subjected to thermal annealing. The wettability alteration has been showed to depend upon both treatments, and insights into how to introduce more stable hydrophilicity into these films have been presented for the sake of boosting their commercial value. Observations from multiple length scales to assess the wetting behavior of as-deposited and high-temperature annealed samples were assessed through macroscopic measurements, i.e., water contact angle measurements, showing that the annealed crystalline samples, treated at 500 degrees C, are much more hydrophilic (SCA approximate to 20 degrees) than as-deposited TiO2 films (SCA approximate to 90 degrees), and the nanoscopic experiments performed by amplitude modulation (AM) atomic force microscopy (AFM) indicated that this increased hydrophilicity is related to an enhanced adhesion force and surface energy, resulting in the partial crystallization of TiO2 and the consequent formation of crystals on its surface rather than being related to morphologic differences. XRD and Raman :measurements have highlighted that the crystallinity of the TiO2 film is crucial in determining its hydrophilicity, in good agreement with the AFM study. The results also indicated that, after irradiation, the samples treated at 500 degrees C preserve their hydrophilicity for a significant time compared to previous studies.