The subject of this research is to explore the possibility of preparation of nanocomposite material of improved thermo-mechanical and tribological properties, using inorganic fullerene-like tungsten disulfide nanostructures (IF-WS2) as reinforcement in poly(vinyl butyral) (PVB). This paper also reports investigation of the effects of using different solvents in preparation of PVB/IF-WS2 nanocomposite on the thermo-mechanical behavior of the resulting material. PVB was dissolved in ethanol, isopropanol, n-butanol and ethyl acetate. IF-WS2 nanoparticles were added to these PVB solutions and dispersed by different deagglomeration techniques. Samples were dried and thin films were obtained. Their microstructure and the quality of IF-WS2 dispersion and deagglomeration in PVE matrix was analyzed by scanning electron microscope (SEM). The reinforcing effect of IF-WS2 is examined by determining hardness, reduced modulus of elasticity and coefficient of friction, by nanoindentation and nanoscratch test, in terms of the different solvents applied in preparation of the samples, mode of stirring and different contents of IF-WS2. The glass transition temperature (T-g) was determined for the prepared samples using differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMA). Storage modulus and mechanical loss factor were observed in a defined temperature range using DMA. (C) 2016 Elsevier B.V. All rights reserved.