We synthesized a planar pDPPTTi-OD polymer based on diketopyrrolopyrrole (DPP) and thieno [2,3-b] thiophene (TTi) and investigated the electrical properties of the pDPPTTi-OD polymer. pDPPTTi-OD films displayed a low optical bandgap of 1.57 eV, and HOMO and LUMO levels of -5.40 and -3.74 eV, respectively. The 150 C-annealed pDPPTTi-OD films showed a high hole mobility of 0.16 cm(2)V(-1)s(-1) in organic thin-film transistor (OTFT) devices. The photovoltaic properties of polymer solar cells (PSCs) incorporating the pDPPTTi-OD were also measured. A pDPPTTi-OD:PC71BM blend film was spin-coated at 25, 70 and 90 degrees C. High-temperature processing significantly improved the power conversion efficiency of PSCs by effectively reducing the PC71BM domain sizes, which improved the miscibility between pDPPTTi-OD and PC71BM. This work demonstrated that the TIT moiety is a useful donor building block for high-performance D-A type polymers in OTFTs and PSCs, and that processing temperatures should be controlled to fully realize the materials' beneficial intrinsic properties. (C) 2016 Elsevier Ltd. All rights reserved.