A slow forming carrier-induced degradation effect has previously been reported for p-type multi-crystalline silicon (mc-Si) solar cells, and has been observed to be most severe in passivated emitter and rear contact (PERC) designs. The as yet undetermined defect (or defects) responsible for this degradation is typically described as being light-induced. However, in this work we confirm that a directly equivalent degradation also occurs when subjecting a cell to current injection, thus the effect can therefore be more accurately described as being carrier-induced. The defect can take years to form under normal operating conditions, but acceleration of this formation and an apparent subsequent passivation through the use of high intensity illumination at elevated temperatures has recently been demonstrated. In this work we further investigate this approach, analyzing the effects of temperature and time on degradation, regeneration, and resulting stability, as well as the variations in treatment response for me-Si materials from two different manufacturers. Susceptibility to carrier-induced degradation after 225 h of light soaking at 70 degrees C is shown to be reduced by 80% using a rapid, 10 s treatment with an illumination intensity of 44.8 kw/m(2) at 200 degrees C. Stability is shown to further improve by extending treatment time but is reduced with increasing treatment temperature. (C) 2016 Elsevier B.V. All rights reserved.