MOF-199 was modified by incorporating activated carbon (AC) during its synthesis under hydrothermal conditions to improve its performance in the removal of hydrogen sulfide (H2S) and dimethyl sulfide (CH3SCH3). A variety of different characterization techniques including X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, nitrogen adsorption/desorption isotherms, scanning electron microscopy (SEM), pyridine adsorption infrared spectroscopy (Py-IR), thermogravimetric-mass spectroscopy (TG-MS) and X-ray photoelectron spectroscopy (XPS) were used to analyze the fresh and exhausted composites. It was found that the composites, which have an amount of AC of less than 2%, had the same morphology as those of pristine MOF-199, but exhibited a more ordered crystallinity structure as well as higher surface area. The composite with 2% AC incorporation showed highest sulfur capacity of 8.46 and 8.53% for H2S and CH3SCH3, respectively, which increased by 51 and 41% compared to that of MOF-199. This improvement was attributed to the formation of more micropores and especially the increased number of unsaturated copper metal sites, as revealed by Py-IR. It is suggested the chemical reaction was apparent during adsorption of H2S, which resulted in the formation of CuS and the collapse of the MOF structure. Whereas reversible chemisorption was found for CH3SCH3 adsorption, as testified by TG-MS and fixed-bed regeneration. Exhausted MAC-2 can be almost totally regenerated by high temperature 180 degrees C nitrogen purge, indicating a promising adsorbent for CH3SCH3 removal. (C) 2016 Elsevier B.V. All rights reserved.