The effects of electrolyte additives on gas evolution, gas consumption and impedance growth at elevated temperature have been studied using Li[Ni0.42Mn0.42Co0.16]O-2 (NMC442)/graphite pouch cells and pouch bags containing delithiated NMC442 or lithiated graphite electrodes plus electrolyte. It was found that there was much more gas, mostly CO2, generated in pouch bags containing charged positive electrodes than pouch cells. It was found that the impedance of the charged positive electrodes stored in pouch bags increased dramatically, while those stored in pouch cells did not. The two observations show that there are interactions between positive and negative electrodes that limit gas evolution and reduce impedance growth in Li-ion cells. To verify this, CO2 intentionally added to pouch bags containing lithiated graphite and electrolyte was consumed. The use of several electrolyte additives, known to affect gassing and high voltage cycling did not substantially alter these conclusions. XPS studies were used to eliminate some possible mechanisms responsible for these phenomena. (C) The Author(s) 2016. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY, http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited. All rights reserved.