Mussel-inspired polydopamine (PDA) coatings have been broadly exploited for constructing functional membrane surfaces. One-step codeposition of PDA with antifouling polymers, especially zwitterionic polymers, has been regarded as a promising strategy for fabricating antifouling membrane surfaces. However, one challenge is that the codeposition is usually a slow process over 10 h or even several days. Herein, we report that CuSO4/H2O2 is able to notably accelerate the codeposition process of PDA with poly(sulfobetaine methacrylate) (PSBMA). In our case, PSBMA is facilely anchored to the polypropylene microporous membrane (PPMM) surfaces within 1 h with the assistance of PDA because of its strong interfacial adhesion. The PDA/PSBMA-coated PPMMs show excellent surface hydrophilicity, high water permeation flux (7506 +/- 528 L/m(2).h at 0.1 MPa), and an outstanding antifouling property. Moreover, the antifouling property is maintained after the membranes are treated with acid and alkali solutions as well as organic solvents. To recap, it provides a facile, universal, and time-saving strategy for exploiting high-efficiency and durable antifouling membrane surfaces.