Nanomaterials of titanium oxide were prepared by pulsed laser ablation of a titanium metal target in distilled water. The ablation was performed at different laser energy (fluence) using a nanosecond pulsed Nd:YAG laser output of 1064 and 532 nm. A post-irradiation of titanium oxide nanocolloids obtained by ablation using 532 nm was carried out to explore its effects on the structure and properties. Analysis of morphology, crystalline phase, elemental composition, chemical state, optical and luminescent properties were performed using Transmission Electron Microscopy (TEM), X-Ray Diffraction (XRD), X-Ray Photoelectron Spectroscopy (XPS), UV-vis absorption spectroscopy and room temperature photoluminescence spectroscopy. It was found that titanium oxide nanomaterial morphologies and optical properties were determined by ablation wavelength and fluence. Further, nanocolloids prepared by 532 nm ablation showed a crystalline phase change by laser post-irradiation. The results showed that pulsed laser ablation in liquid as well as post-irradiation were effective in modifying the final structure and properties of titanium oxide nanocolloids. (C) 2017 Elsevier B.V. All rights reserved.