Adhesive cementation of bonded all-ceramic restorations is critical for their long-term clinical performance. The objective of this study was to evaluate the role of post-etch cleaning (PEC) and silane heat treatment on the micro-tensile bond strength of silica-based leucite (SBLE) ceramic when bonded to composite resin. Twenty-four blocks of SBLE ceramic (HeraCeram Press (R),Heraeus Kulzer GmbH Gruner Weg 11 63450 Hanau) were fabricated and bonding surfaces were etched using 9.5% hydrofluoric acid. Six experimental groups were made from the various surface treatment combinations including: PEC (37.5% phosphoric acid for 1 min, rinsed with water for 20 s and ultrasonic bath immersion), silane application and silane heat treatment (100 degrees C for 5 min). An adhesive resin and a light-cured restorative composite were used to bond the ceramic and composite resin blocks under standard conditions. Three hundred and sixty specimen sticks (8 x 1 mm(2)) were subjected to micro-tensile testing. The means of the micro-tensile bond strength (mu-TBS) were analysed with ANOVA and Tukey-Kramer multiple comparison test. The specimens tested were assessed for mode of failure using scanning electron microscopy. The highest mu-TBS value (38.25 +/- 3.40 MPa) of the specimen was achieved by PEC and heated silane. PEC and silane application showed statistically significant improvements in the mu-TBS (p < 0.01). The mean maximum difference was due to PEC (18.91 +/- 3.70 MPa). In the surface treatment of SBLE ceramics, PEC had the most significant factor which affected the mu-TBS of resin composite.