Electrodes of Proton Exchange Membrane Fuel Cells (PEMFCs), consisting of catalyst-coated gas diffusion layers, were subjected to an optimized ion exchange procedure, in which tin (IV) oxide (SnO2) nano particles were introduced into them. Both methanol and sulfuric acid were tested as ion exchange solvents. SnO2 has previously been shown to exhibit radical scavenging abilities towards radicals inside the electrocatalyst layers. Its presence inside the electrodes was confirmed using X-ray photoelectron spectroscopy and X-ray fluorescence. After exposure to an accelerated stress test in a three-electrode setup, the electrodes containing SnO2 were found to have retained approximately 73.0% of their original Pt, while only 53.2% was retained in electrodes treated identically, but without Sn. Similarly, the SnO2-treated electrodes also experienced a smaller loss in electrochemical surface area in comparison to before the accelerated stress test. A membrane electrode assembly (MEA) constructed with a SnO(2-)containing anode was evaluated over 500 h. The results showed remarkably reduced OCV decay rate and end of test hydrogen crossover compared to the control MEA, indicating that SnO2 aids in impeding membrane thinning and pinhole formation. The results point toward a positive effect of SnO2 on fuel cell durability, by reducing the degradation of the membrane as well as of the ionomer in the electrocatalyst layer.(C) 2017 Elsevier B.V. All rights reserved.