Recently, sodium-ion batteries (SIBs) have been considered as the promising alternative for lithium-ion batteries. Although layered P2-type transition metal oxides are an important class of cathode materials for SIBs, there are still some hurdles for the practical applications, including low specific capacity as well as poor cycling and rate properties. In this study, the electrochemical properties of layered Mn-based oxides have been effectively improved via Al doping, which cannot only promote the formation of layered P2-type structure in the preparation processes but also stabilize the lattice during the successive Na-intercalation/deintercalation due to suppression of the Jahn-Teller distortion of Mn3+. Among the as prepared series of Na2/3Mn1-xAlxO2 (x = 0, 1/18, 1/9, and 2/9), Na2/3Mn8/9Al1/9O2 with x = 1/9 exhibits the optimal doping effect with the best electrochemical properties, in terms of the highest specific capacity of 162.3 mA h g(-1) at 0.1 C, the highest rate capability, and the best cycling stability in comparison to the undoped Na2/3MnO2 and the other two materials with different Al-doped contents. Both cyclic voltammetry at varied scan rates and galvanostatic intermittent titration technique disclose the optimal electrode kinetics (the highest Na-diffusion coefficient) of the best Na2/3Mn8/9Al1/9O2. (C) 2017 Elsevier B.V. All rights reserved.