Micron -sized nanoporous silver powder with pore size of similar to 400-160 nm and specific surface area of similar to 4.7-5.5 m(2)/g was synthesized from three mechanically alloyed Ag-Zn powders (composition: 25, 50 and 75 at.% Zn). Dealloying was carried out at free corrosion conditions in NaOH, HCl and AgNO3 solutions. Both partial and complete dealloying were obtained by suitable choice of electrolyte and time of exposure. Zn in the solution after dealloying was recovered in the form of ZnO nanoparticles with particle size of 55.7+/-18 nm. The effect of composition and electrolyte on the degree of dealloying was also studied. (C) 2017 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.