We report the synthesis of carnation flower-like SnS2 (CF-SnS2) via a one-step solvothermal method for potential application as supercapacitor electrodes in energy storage devices. The structural and morphological properties of CF-SnS2 were characterized by X-ray diffraction, Raman analysis, and field-emission scanning and transmission electron microscopies. X-ray photoelectron spectroscopy and scanning tunneling electron microscopy with color mapping verified the distribution of Sn and S, and depicted the successful formation of SnS2. Electrochemical studies were performed to explore the supercapacitive nature of CF-SnS2. Supercapacitors with CF-SnS2 electrodes delivered excellent cyclic voltammetry performances, superior gravimetric specific capacitances, and high power densities. The evaluated specific capacitance and power density reached similar to 524.5 F/g and 12.3 W/kg, respectively, at a current density of 0.08 A/g, and similar to 215.9 F/g and 61.4 W/kg, respectively, at a current density of 0.38 A/g. These values are at least two times higher than those previously reported. The long-term cyclic stability was also tested to demonstrate the endurance of the CF-SnS2-based supercapacitor, with a 66% rate retention and galvanostatic charge/discharge reversibility. These electrochemical findings indicate that CF-SnS2 is a promising candidate for electrode materials in supercapacitor applications. (C) 2017 Elsevier B.V. All rights reserved.