Graphite and graphene particles were used to reinforce the electrical conductivity and anti-corrosion properties of polyurethane (PU) coatings. The effect of graphite and graphene were compared. Hybrid filler using carbon nanotube was adopted as well and the performance in electrical conductivity was much superior to single filler system. At the same filler loading, the electrical conductivity of hybrid filler system was significantly higher than single filler system (0.77 S/m at 5 wt% while single filler system was not conductive). The conductive mechanism was revealed. In terms of anti-corrosion properties, the coatings with low filler loading had better anti-corrosion properties. The resistance values obtained from EIS (Electrochemical Impedance Spectroscopy) and four point probe method were compared and discussed. (C) 2017 Elsevier B.V. All rights reserved.