Series of transition metal-doped TiO2 (metal/TiO2) is prepared by combining the hydrothermal synthesis and air-thermal treatment without any reduction process. The selected transition metal precursors, including Ag, Au, Co, Cr, Cu, Fe, Ni, Pd, Pt, Y, and Zn, were individually doped into TiO2 nanofibers to evaluate the photocatalytic degradation activity and photocatalytic hydrogen generation. Consider the photocatalytic performance of these synthesized metal/TiO2 under UV-A irradiation, copper doped TiO2 nanofibers (Cu/TiO2 NFs) was chosen for further study due to its extraordinary reactivity. Systematical studies were spread to optimize the doping concentration and the calcination condition for much higher photocatalytic activity Cu/TiO2 NFs. In the photocatalytic degradation test, 0.5 mol%-Cu/TiO2 NFs calcined at 650 degrees C exhibits the highest activity, which is even higher than commercial TiO2-AEROXIDE (R) TiO2 P25 under UV-A irradiation. The synthesized 0.5 mol%-Cu/TiO2-650 NFs also have the capability in the photocatalytic hydrogen production. The hydrogen evolution rates are 200 mu mol/g.h under UV-A irradiation and 280 mu mol/g.h under UV-B irradiation. The density of state calculated by CASTEP for Cu/TiO2 indicates that Cu doping contributes to the states near valence band edge and narrows the band gap. The disclosed process in this study is industrial safe, convenient and cost-effective. We further produce a significant amount of TiO2-based catalysts without any hydrogen reduction treatment. (C) 2017 Elsevier B.V. All rights reserved.