A fast and facile protocol is reported aiming at improving the antifouling property and hemocompatibility of poly(vinylidene fluoride) (PVDF) membranes by tethering PEG hydrogel and zwitterion immobilization. The coated PEG hydrogel was first prepared by interfacial polymerization and tethered on an alkali treated PVDF membrane (PVDFA) surface via a simultaneous thio-ene and thiol-epoxy reaction. Then, the thiol groups of cysteine reacted with the epoxy groups in PEG hydrogel to fabricate the PVDFA-g-Cys membrane. The membrane fabrication was complete within less than 20 min and was conducted in mild conditions. The successful preparation of PVDFA-g-Cys membrane was confirmed by ATR-FTIR and XPS. Raman spectroscopy showed that the hydrogels covalently bonded to the PVDF membrane surface. The membrane retained its mechanical strength after modification. The SEM measurements suggested that the membrane became denser after hydrogel coating, meanwhile, the EDX test verified that the functional species uniformly distributed in the membrane matrix. Water contact angle (WCA), protein adsorption and protein filtration tests showed significant improvements in hydrophilicity and antifouling properties for the modified membrane. The negativity of the membrane surface measured by the streaming potential method provides a basis for protein resistance and hemocompatibility. Moreover, the suppressed platelet adhesion and prolonged plasma coagulant time show that the PVDFA-g-Cys membrane has ultralow thrombotic potential and better hemocompatibility. The reported surface modification method combing thio-ene and thio-epoxy chemistry not only facilitates fabrication of hemocompatible PVDF membrane but also provide an universal chemical platform for multifunctionalization of porous membranes. (C) 2017 Elsevier B.V. All rights reserved.