In the present study, Nb2O5 (NZ0) composite coatings with various concentrations of zinc (NZ2, NZ4 & NZ6) are produced on 316L SS by sol-gel method with the aim of improving its antibacterial activity, bone formability and corrosion resistance properties. This work studied the surface characterization of NZ0, NZ2, NZ4 & NZ6 coated 316L SS by ATR-FTIR, XRD, HR-SEM with EDAX. The synthesized coatings were different in the morphological aspects, NZ0 shows mesoporous morphology whereas irregular cluster like morphology was observed for the zinc incorporated coatings. The chemical composition of the NZ0 and NZ4 composite coatings were studied by XPS and the results revealed that the zinc exist as ZnO and Nb as Nb2O5 in the coatings. The increase in the concentration of zinc in Nb2O5 increases the hydrophilic nature identified by water contact angle studies. The potentiodynamic polarization studies in simulated body fluid reveals the increase in polarization resistance with decrease in current density (i(corr)) and electrochemical impedance spectroscopic studies with increase in charge transfer resistance (R-ct) and double layer capacitance (Q(dl)) were observed for NZ4 coated 316L SS. The inhibition of Staphylococcus aureus and Escherichia coli bacteria were identified for NZ4 coated 316L SS by bacterial viability studies. The NZ4 coated 316L SS showed better Osseo-integration by spreading the MG 63 osteoblast cells. The study results imply that zinc incorporated Nb2O5 (NZ4) composite coating exhibits antibacterial activity and also enhance the corrosion resistance and biocompatibility of the 316L SS. (C) 2017 Published by Elsevier B.V.