For the sake of improving the charring performance and flame retardancy of epoxy resin (EP), boron-containing phenolic resin (BPR) instead of a conventional curing agent, linear phenolic resin (LPR) was employed to cure EP. Of several possible chemical structures for BPR, the existence of benzyl hydroxy groups in BPR chains has been confirmed using H-1 nuclear magnetic resonance spectroscopy. The resonance of these groups may reasonably explain the higher curing reactivity of BPR-cured EP than that of LPR-cured EP. Thermogravimetric analysis, observation of the morphologies of the char residues and X-ray photoelectron spectroscopic were performed to characterize the charring process. Due to the presence of B2O3 produced on the char surface from decomposition of phenyl borates and the facile high self-crosslinking reaction of BPR, a more continuous and stronger char barrier was formed for BPR-cured EP compared to that for the LPR-cured EP system. Therefore the former exhibited much better flame retardancy. In addition, BPR-cured EP also displayed better dynamic mechanical properties, than those observed for LPR-cured EP. It is not subject to the significant lowering the glass transition temperature of the polymer which accompanies curing with LPR. This suggests that BPR cured resin may meet the requirement for utilization at high temperature. (C) 2017 Published by Elsevier B.V.