Piezoelectric materials have been widely used in various applications, such as high-voltage sources, actuators, sensors, motors, frequency standard, vibration reducer, and so on. In the past decades, lead zirconate titanate (PZT) binary ferroelectric ceramics have dominated the commercial piezoelectric market due to their excellent properties near the morphotropic phase boundary (MPB), although they contain more than 60% toxic lead element. Here, we report a lead-free and one-composition molecular ferroelectric trimethylbromo-methylammonium tribromomanganese(II) (TMBM-MnBr3) with a large piezoelectric coefficient d(33) of 112 pC/N along polar axis, comparable with those of typically one-composition piezoceramics such as BaTiO3 along polar axis [001] (similar to 90 pC/N) and much greater than those of most known molecular ferroelectrics (almost below 40 pC/N). More significantly, the effective local piezoelectric coefficient of TMBM-MnBr3 films is comparable to that of its bulk crystals. In terms of ferroelectric performance, it is the low coercive voltages, combined with the multiaxial characteristic, that ensure the feasibility of piezo film applications. Based on these, along with the common superiorities of molecular ferroelectrics like light weight, flexibility, low acoustical impedance, easy and environmentally friendly processing, it will open a new avenue for the exploration of next generation piezoelectric devices in industrial and medical applications.