Superparamagnetic nanoparticles with a high initial magnetic susceptibility chi(degrees) are of great interest in a wide variety of chemical, biomedical, electronic, and subsurface energy applications. In order to achieve the theoretically predicted increase in chi(degrees) with the cube of the magnetic diameter, new synthetic techniques are needed to control the crystal structure, particularly for magnetite nanoparticles larger than 10 nm. Aqueous magnetite dispersions (Fe3O4) with a chi(degrees) of 3.3 (dimensionless SI units) at 1.9 vol %, over 3- to 5-fold greater than those reported previously, were produced in a one-pot synthesis at 210 degrees C and ambient pressure via thermal decomposition of Fe(II) acetate in triethylene glycol (TEG). The rapid nucleation and focused growth with an unusually high precursor-to-solvent molar ratio of 1:12 led to primary particles with a volume average diameter of 16 nm and low polydispersity according to TEM. The morphology was a mixture of stoichiometric and substoichiometric magnetite according to X-ray diffraction (XRD) and Mossbauer spectroscopy. The increase in chi(degrees) with the cube of magnetic diameter as well as a saturation magnetization approaching the theoretical limit may be attributed to the highly crystalline structure and very small nonmagnetic layer (similar to 1 nm) with disordered spin orientation on the surface.