Korean Chemical Engineering Research, Vol.56, No.2, 156-161, April, 2018
제조방법에 따른 TiO2의 광촉매 특성 분석
Photocatalytic Properties of TiO2 According to Manufacturing Method
E-mail:
초록
염소법과 졸-겔법으로 TiO2 광촉매 분말을 제조하였다. 제조방법 및 조건에 따라 촉매의 결정상 형태(아나타제와 루타일)와 비표면적이 변화하는 것을 알 수 있었다. TTIP-sol로 제조한 광촉매가 염소법이나 TBOT-sol로 제조한 광촉매에 비해 methylene blue (MB) 분해 특성이 더 높았으며, 수용액상의 90% 이상의 MB를 제거할 수 있었다. 실험 결과를 통해 TiO2 광촉매는 단일 아나타제상와 큰 비표면적을 가지면 유기물 분해 특성을 향상될 수 있는 것을 확인하였다.
TiO2 photocatalyst powders were prepared by chlorination method and sol-gel method. Specific surface area and crystalline (i.e., anatase and rutile) of the catalyst varied depending on manufacture conditions and method. TTIP-sol photocatalyst had higher methylene blue (MB) decomposition characteristics than photocatalyst from chlorination method and TBOT-sol. MB removal efficiency from aqueous solution with TTIP-sol photocatalyst was over 90%. Experimental results showed that the TiO2 photocatalyst with a single anatase phase and a large specific surface area had high decomposition characteristics of organic materials.
- Pyo SH, Kim MJ, Lee SC, Yoo CK, Korean Chem. Eng. Res., 52(4), 503 (2014)
- Andreozzi R, Caprio V, Insola A, Marotta R, Catalysis Today, 53(1), 51 (1999)
- Fukahori S, Ichiura H, Kitaoka T, Tanaka H, Enviro. Sci. Technol., 37, 1048 (2003)
- Jihoon J, Theor. Appl. Chem. Eng., 12, 1427 (2006)
- Kim Y, Bai BC, Lee YS, Appl. Chem. Eng., 23(3), 308 (2012)
- Athanasekou CP, Moustakas NG, Morales-Torres S, Pastrana-Martinez LM, Figueiredob JL, Faria JL, Silva AMT, Dona-Rodriguez JM, Romanos GEM, Falaras P, Appl. Catal. B: Environ., 178, 12 (2015)
- Jia J, Li D, Wan J, Yu X, J. Ind. Eng. Chem., 33, 162 (2016)
- Vautier M, Guillard C, Herrmann JM, J. Catal., 201(1), 46 (2001)
- Cheon MS, Yang OB, Chung HH, Back SK, Appl. Chem., 4(1), 149 (2000)
- Yu W, Yuan S, Li Y, Zhang Q, Wang H, Mater. Res. Bull., 36, 1957 (2001)
- Bacsa RR, Gratzel M, J. Am. Ceram. Soc., 79, 2185 (1996)
- Kim DS, Han SJ, Kwak SY, J. Colloid Interface Sci., 316(1), 85 (2007)