Sandwich-structured carbon nanotubes, silicon oxide, and polyaniline (hereafter denoted as CNTs/SiOx/PANI) were prepared by combining a sol-gel method, magnesiothermic reduction at 250 degrees C, and chemical oxidative polymerization. The CNTs, SiOx and PANI in the composite was 16 wt%, 51 wt% and 33 wt%, respectively. The CNTs/SiOx/PANI electrodes exhibited excellent cycle and high-rate performance as anodes in Li-ion batteries, including charge/discharge capacities of 1156/1178 mAh g(-1) after 60 cycles at 0.2 A g(-1) current density and 728/725 mAh g(-1) at 8 A g(-1) current density. The improvement was due to the synergy between CNTs and PANI. The SiOx scattered on the CNTs core and coated by PANI improved its conductivity and accommodated the volume change during repeated lithiation/delithiation cycles. This simple synthesis provided a scalable route for the large-scale production of CNTs/SiOx/PANI nanostructures, with various applications such as in Li-ion batteries. (C) 2018 Elsevier B.V. All rights reserved.