In this paper, the gas nitrocarburizing technique was applied for the first time to solve the challenge in crack healing of metallic materials. The crack-healing behavior of 42CrMo steel was investigated. The gas nitrocarburizing was carried out in two steps with the decrease of the healing temperature. The mechanical properties after healing were measured using the three-point blending test. X-ray diffraction, optical microscope and scanning electron microscopy were applied to characterize the phase composition and microstructure of crack healing area and analyze healing mechanisms involved. The results show that the optimal healing effect could be obtained when it is healed at 760 degrees C for 2 h and then at 550 degrees C for 4 h. The maximum healing degree reached to 63.68%. The crack healing process could be divided into two stages, i.e. healing in crack tips at high temperatures and then in crack openings at low temperatures. The volumetric expansion and filling of formed nitrides contributed to the rapid healing of the large-sized cracks. The healing efficiency could be improved by decreasing the healing temperature. Moreover, high pressure gas nitrocarburizing was considered as another potential way to improve the healing efficiency and healing degree. (C) 2018 Elsevier B.V. All rights reserved.