Copper sulfide is an important multifunctional semiconductor that has attracted considerable attention owing to its outstanding properties and multiple applications, such as energy storage and electrochemical energy conversion. This paper describes a cost-effective and simple low-temperature solution approach to the preparation of copper sulfide for supercapacitors (SCs) and quantum-dot sensitized solar cells (QDSSCs). X-ray diffraction, X-ray photoelectron spectroscopy, and transmission electron microscopy confirmed that the nickel foam with a coriander leaf like nanostructure had been coated successfully with copper sulfide. As an electrode material for SCs, the CC-3 h showed excellent specific capacitance (5029.28 at 4 A g(-1)), energy density (169.73 W h kg(-1)), and superior cycling durability with 107% retention after 2000 cycles. Interestingly, the QDSSCs equipped with CC-2 h and CC-3 h counter electrodes (CEs) exhibited a maximum power conversion efficiency of 2.52% and 3.48%, respectively. The improved performance of the CC-3 h electrode was attributed mainly to the large surface area (which could contribute sufficient electroactive species), good conductivity, and high electrocatalytic activity. Overall, this work delivers novel insights into the use of copper sulfide and offers an important guidelines for the fabrication of next level energy storage and conversion devices. (C) 2017 Elsevier B.V. All rights reserved.