On the way to sodium-based all-solid-state batteries, interface analysis is a key issue. In this work, the interface between two typical solid sodium-ion conductors (Na-beta ''-Al2O3 and NASICON) and the layered oxide material NaCoO2 is investigated. The formation of the interface between the electrolyte material and the NaCoO2 coating is studied using an in-situ X-ray photoemission spectroscopy (XPS) surface science approach. Only a slight reduction of zirconium and scandium in NASICON was observed in proximity to the cathode side interface, while severe reactions, including the formation of a CaO-Al2O3 mixed phase, were detected between Na-beta ''-Al2O3 and NaCoO2. (c) 2018 Elsevier Ltd. All rights reserved.