Korean Journal of Chemical Engineering, Vol.35, No.7, 1542-1546, July, 2018
Effects of polydimethylsiloxane coating of Ni-MOF-74 on CH4 storage
E-mail:
Ni-MOF-74 was prepared by microwave heating and coated with polydimethylsiloxane (PDMS) via vapor deposition. Both the pristine and the PDMS-coated Ni-MOF-74 samples were exposed to moisture in air (relative humidity of 75%) for different periods of time, and their methane storage capacities under 35 bar conditions were measured. The pristine sample had a Brunauer-Emmett-Teller (SBET) surface area of 1,050m2ㆍg-1, with a CH4 uptake capacity of 113.8 mgㆍg-1 at 300 K and 35 bar. After exposure to moisture for seven days, the BET surface area and CH4 uptake capacity declined drastically, whereas the PDMS-coated sample maintained its original BET surface area (1,018m2ㆍg-1) and CH4 uptake capacity (107.7mgㆍg-1). After exposure to moisture in air for 30 days, however, even the PDMS-coated sample lost almost 60% of its CH4 storage capacity. All the methane storage capacity data were linearly correlated with the BET surface areas of the Ni-MOF 74 samples.
- Ferey G, Chem. Soc. Rev., 37, 191 (2008)
- Mason JA, Veenstra M, Long JR, Chem. Sci., 5, 32 (2014)
- Pucker J, Zwart R, Jungmeier G, Biomass Bioenerg., 38, 95 (2012)
- Wang XS, Ma S, Rauch K, Simmons JM, Yuan D, Wang X, Yildirim T, Cole WC, Lopez JJ, de Meijere A, Zhou HC, Chem. Mater., 20, 3145 (2008)
- Ma SQ, Sun DF, Simmons JM, Collier CD, Yuan DQ, Zhou HC, J. Am. Chem. Soc., 130(3), 1012 (2008)
- Wu H, Zhou W, Yildirim T, J. Am. Chem. Soc., 131(13), 4995 (2009)
- Getman RB, Bae YS, Wilmer CE, Snurr RQ, Chem. Rev., 112(2), 703 (2012)
- Valenzano L, Civalleri B, Chavan S, Palomino GT, Arean CO, Bordiga S, J. Phys. Chem. C, 114, 11185 (2010)
- Kizzie AC, Wong-Foy AG, Matzger AJ, Langmuir, 27(10), 6368 (2011)
- Zhang W, Hu YL, Ge J, Jiang HL, Yu SH, J. Am. Chem. Soc., 136(49), 16978 (2014)
- Huang G, Yang Q, Xu Q, Yu SH, Jiang HL, Angew. Chem.-Int. Edit., 55, 7379 (2016)
- Zhang G, Zang X, Li Z, Wang C, Wang Z, Talanta, 129, 600 (2014)
- Park EJ, Cho YK, Kim DH, Jeong MG, Kim YH, Kim YD, Langmuir, 30(34), 10256 (2014)
- Lee YR, Jang MS, Cho BY, Kwon HJ, Kim S, Ahn WS, Chem. Eng. J., 271, 276 (2015)
- Wu X, Bao Z, Yuan B, Wang J, Sun Y, Luo H, Deng S, Microporous Mesoporous Mater., 180, 114 (2013)
- Makal TA, Li JR, Lu W, Zhou HC, Chem. Soc. Rev., 41, 7761 (2012)