In this paper, we demonstrate a simple approach to improve the electrochromic performances of polyaniline (PANI) by incorporating PANI nanofibers (PANI-NFs) synthesized by interfacial polymerization into water-soluble PANI:poly(styrene sulfonate) (PANI:PSS). The one-dimensional PANI-NFs endow spin-coated PANI film high electrochemical activities and electrochromic properties. The structures and morphologies of PANI-NFs were characterized by FTIR spectroscopy and SEM observation. The electrochemical behaviors of PANI/PANI-NFs composites were analyzed by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The electrochromic properties of composites were tested using electrochemical working station combining a UV-Vis spectrometer. The results show that the PANI-NFs with even diameter of similar to 30 nm can be synthesized easily using interfacial polymerization method. With the increasing of feeding amount of PANI-NFs, the oxidation peaks of CV curves shift to low potential direction, indicating enhanced electrochemical activities. The electrochromic test confirms that the PANI/PANI-NFs composites films have higher electrochromic contrast of 0.67 as comparison to 0.49 of PANI:PSS film. The PANI/PANI-NFs also exhibit excellent electrochromic stability. After 2000 cycles switching, only less than 4% contrast decay is observed. The enhanced electrochromic properties can be attributed to the small charge-transfer resistance and facile ion diffusion process brought by PANI-NFs. The EIS tests exhibit that with incorporating of highly conductive PANI-NFs, the PANI/PANI-NFs composites possess relatively lower charge-transfer resistance of 76 Omega as comparison to 94 Omega of neat PANI:PSS. [GRAPHICS] .