Neutron Reflection (NR) and Dynamic Secondary Ion Mass Spectroscopy (DSIMS) experiments were conducted on symmetrically deuterated polystyrene triblock bilayers (HDH/ DHD) which directly probed the interdiffusion dynamics of the chains during welding. The HDH chains had their centers deuterated 50%, the DHD chains had their ends deuterated (25% at each end) such that each chain contained approximately 50% D. During welding, anisotropic motion of the chains produces a time-dependent oscillation (ripple) in the H and D concentration at the interface, which bears the characteristic signature of the polymer dynamics. These oscillations were compared with those predicted by Rouse, polymer mode coupling (PMC), and reptation dynamics. The following conclusions can be made from this study. (a) During the interdiffusion of high molecular weight HDH/DHD pairs, higher mobility of the chain ends caused a concentration oscillation which increased to a maximum amplitude, and eventually vanished at times, t > tau(D). The amplitude, or excess enrichment found, was appreciably more than that predicted by Rouse and PMC simulations, and was only slightly less than that predicted from reptation simulations. (b) The oscillations were completely missing in the 30 and 50K HDH/DHD polymers, which are only weakly entangled. The lack of oscillations for the 30 and 50K pairs may be due to a combination of surface roughness and fluctuations of order 30 Angstrom. (c) It was found that the position of the maximum in this ripple stayed at the interface during its growth. This is also consistent with reptation and has not been explained by other theories. (d) All dynamics models for linear polymers produce ripples, many of which are qualitatively similar to that predicted for reptation However, each ripple bears the fingerprint of the dynamics in terms of its time-dependent shape, position, and magnitude, and the models are clearly distinguishable. Our results, in summary, support reptation as a candidate mechanism of interdiffusion at polymer-polymer interfaces and its uniqueness is being further pursued.