Electrolytic manganese dioxides (EMDs) were prepared on the 100 g scale by anodic deposition from acidic aqueous solutions of manganese sulfate. In situ doping with titanium ions was achieved by addition of tetra-n-butoxytitanium to the electrolytic bath. Samples were also doped ex situ by washing the products with aqueous barium hydroxide solution. The EMDs were characterized by electron microscopy studies and BET surface area determinations. Cyclic abrasive stripping voltammetry was successfully applied to evaluate the rechargeability of the newly synthesized undoped and doped EMDs in 9 M KOH. Relative discharge capacities at different depths of discharge (DOD) with respect to the first one-electron reduction of gamma-MnO2 are compared for different EMDs. At about 30% DOD, resulting relative discharge capacities show essentially the same trend as those measured in AA cells from about 10 to 20 discharge/charge cycles onwards. Accordingly, titanium-doped EMD was shown to exhibit superior charge retention and rechargeability when compared to the titanium-free samples.